Filament Roffelsen3D PA6 CF15
Extruded Polyamide 6 (PA6) reinforced with 15% carbon fibres for 3D printing with enhanced mechanical properties. The carbon fibres significantly improve the strength and rigidity of the filament making it suitable for applications that require parts with high stiffness and durability. Additional advantages of the filament are heat and chemical resistance. This high performance filament was developed for industrial use and engineering/functional parts.
3D processing method: FFF (Fused Filament Fabrication)
Diameter (mm): 1.75
Form: wound on a spool (app 354/133 m per 1 kg of 1,75 mm filament)
Packaging: packed in a hermetically sealed plastic bag with silica gel
Color: black
3D printing profiles
Printing conditions
Processing Method: FFF (Fused Filament Fabrication)
Drying (hours/°C): 16-24/70. Dry before every use. Filament should be kept dry also during printing (should not be able to absorb humidity). Store in a closed bag in a dry place.
Dry box: recommended
Adhesion: for glass we recommend using glue.
Nozzle size (mm) and type: ≥ 0,6, hardened
Nozzle Temperature (°C): 265-290. For the best mechanical properties print at the higher end of temperature range, i.e. in the 280-290°C range.
Speed (mm/s): 45-60
Bed Temperature (°C): 70-110
Build chamber: closed
Heated chamber (°C): tba
Active cooling (%): 0-10
| Colors | Black |
|---|---|
| BambuLab AMS | Yes |
| Weight | 750g |
| Country of origin | European Union |
| String diameter | 1,75mm |
| Temperature Nozzle °C | 265-290 |
| Bed Temperature °C | 70-110 |
| Nozzle type (recommended) | Hardened |
| Closed chamber | It's recommended |
| Diameter tolerance | ± 0,02 mm |